The microstructural changes and crack propagation in the carburized layer of SUS304 stainless steel due to repeated vacuum carburizing
quenching as a heat treatment basket were investigated in this paper. As a result, beneath a graphite scale formed on the outermost surface,
it was revealed that there were three types of carburized layers with different morphologies: M7C3 layer, M7C3/M23C6 mixed layer, and M23C6
layer (M = Cr, Mn, Fe). In addition, the surface was found to be uneven due to the occurrence of metal dusting. Besides, repeated heating and
quenching caused the formation of voids in carbides and matrix in the carburized layer, and micro cracks appeared in the surrounding areas.
Under the loading stress during vacuum carburizing quenching, these voids, micro cracks, and the uneven surface are considered to be the initial points for cracking.